本研究為設計一階級薄板(2mm、4mm及6mm)，來探討製程參數對薄壁球墨鑄鐵件之影響。首先在相同的碳當量(目標值4.8%)下，針對接種劑和球化劑的種類與添加量對不同厚度(2mm、4mm及6mm)的薄壁球墨鑄鐵件組織均勻性之探討。其次，在相同的碳含量(目標值3.9%)下，探討矽含量、接種劑與球化劑之種類及添加量與鑄模塗層等製程參數對於球墨數、球化率、肥粒鐵百分率及碳化物百分率等組織均勻性與抗拉機械性質之影響。
實驗結果顯示，在較高的碳當量(約4.6%~4.8%)下，以濕砂模可成功製造出2mm厚(70mm×60mm)的低碳化物(5%以下)薄壁球墨鑄鐵件。
欲獲得較佳組織均勻性及抗拉機械性質之薄壁球墨鑄鐵件，其製程條件為: C.E.值控制為4.66%(3.67%C，2.97%Si)、模穴有上塗層(石墨液)、添加1.0%的 S-70接種劑及1.0%的C.G.球化劑。2mm厚度之鑄件其球墨數可達2673/mm2以上，球化率可達90%。基地肥粒鐵百分率可達76%以上，碳化物百分率低於5%。平均抗拉強度可達
56 kg/mm2，伸長率為7%。

The primary purpose of this research was to nvestigated the effects of molten metal processing variables on the stepped thin-wall ( 2, 4 and 6 mm in thickness ) ductile iron castings. First, the carbon equivalent ( 4.8 % ) was controlled, the effects of homogeneous microstructure on the stepped thin-wall ductile iron castings with various inoculants, spheroidizer and their addition amount was investigated. Second, at the same carbon content ( 3.9 % ), to study the effects of processing variables, such as, addition amount of Si, type of inoculants and its addition amount, spheroidizing treatment, solidification cooling rate and mold coating on the microstructure and mechanical properties of the thin-wall ductile iron castings.

The experimental results show that production of the thin-wall ( 2 mm in thickness ) ductile iron castings with carbide fraction less than 5 % was successful by using green sand mold at higher ( 4.6 % ~ 4.8 % ) carbon equivalent.

To get thin-wall ductile iron castings with better homogeneous microstructure and mechanical properties, the processing variables are carbon equivalent under 4.66 % ( 3.67 % C, 2.97 % Si ), mold cavity with graphite coating, adding 1.0 % inoculant S-70 and 1.0 % spheroidizer C. G. The nodule count and nodularity of the castings with 2mm thickness can be up to 2673/mm2 and 90%. The ferrite fraction of matrix can be up to over 76 %, the carbide fraction under 5 %, the average ultimate tensile strength up to 56 kg/mm2, and 7 % elongation.

1.潘永寧，“新鑄鐵材料的發展”，高品質鑄鐵講習會，工業技術研究院工業材料所，1991。
2. J.F. Cuttino, J.R. Andrews and T.S. Piwonka, Development in Thin-Wall Iron Casting Technology”, AFS Trans. Vol 107, 1999, pp.363-372.
3. J.M. von Wurtemberg , “Lightweight Materials for Automotive Applications ”, SinterCast S.A., Feb, 1994.
4. S. Katz, “Thin-Wall Iron Castings—Planning the Future”, Foundry Management and Technology, June, 1997, pp.34-36.
5. A. Javaid, J. Thomson, M. Sahoo and K.G. Davis, “Factor Affecting the Formation of Carbides in Thin-Wall DI Castings”, AFS Trans. Vol 107, 1999, pp.441-456.
6. Amjad Javaid, Keith G. Davis and Mahi Sahoo, “Mechanical Properties in Thin-Wall Ductile Iron Castings”, Moderm Casting, June, 2000, pp.39-41.
7. J.L.Davis, and J. Begg, “Dimensional Accuracy and Mechanical Properties of Thin-Section Gray Iron Castings”, BCIRA Technology, Report No. 9208, Nov, 1992.
8. “Production of Very Thin-Section Iron Castings, Final Report for the Period 1992-1995”, BCIRA, 1995.
9. G.van der Graaf, H.E.A. van den Akker and L. Katgerman, “Flow Phenomena of Mold Filling for Thin-Wall Iron Castings”, 60 th World Foundry Congress, Sep 26, 1996.
10. P.C.van Eldijk, J. Kaspers, H. van Lipzig and J.int Velt, “Thin Ductile Iron Castings, for Automotive Applications; A Strong Potential”, 60 th World Foundry Congress, Sep 26, 1996.
11. G.D. Chandley, and D.L.Cargill, “Thin-Walled Castings by the CLV Process”, AFS Trans. Vol. 98, 1990, pp.413-416.
12. P. Purdom ,“Thin-Wall Iron Castings”, Foundry Trade Journal, Apr 3, 1992.
13. P. Purdom, “High Volume Process for Thin-Wall Iron Castings”, Automotive Technology, Ltd. , Mar, 1992, p.169.
14. K. Hornung, “Thin-Section Ductile Iron Castings”, 61 st World Foundry Congress (Technical Forum), 1995, pp.75-83.
15. William L. Tordofr, “Hybrid Casting Process Produces Thin-Wall Ferrous Components”, Moderm Casting, Nov, 1999, pp.58-59.
16.張晉昌，“鑄造學”，全華科技圖書，1996。
17. R.S. Lee, and A.P. Volkmar, “Effect of the Mold on Casting Soundness”, AFS Trans., Vol. 85, 1977, p.289.
18. R. Voigt, et al., “Casting Dimensional Control and Fatigue Life Prediction for Permanent Mold Casting Dies”, Technical Progress Report for the Period Sep 29, 1994-Sep 30, 1995, Delivered to the Department of Energy under Contract No. DE-FC07-93ID13235, Nov 1, 1995.
19. F.E. Peters, R. Velaga and R.C. Voigt, “Assessing Dimensional Repeatability of Metalcasting Processes”, AFS Trans. Vol. 104, 1996, pp.181-190.
20. F. Mampaey, Z.A. Xu, “Mold Filling and Solidification of a Thin-Wall Ductile Iron Castings”, AFS Trans. Vol. 107, 1999, pp95-103.
21. Jan-Roel van der Sluis, Steve lllingworth, “塗料對球墨鑄鐵件邊緣部位石墨組織的影響”，鑄造設備與技術，中國鑄造學會，1998，pp.18-23。
22.“Ductile Iron Handbook”, American Foundrymen’s Society , Inc., 1992.
23. Stephen Istvan Karsay, “Ductile Iron Production Practice”, AFS Trans. Vol. 83, 1975.
24.“球墨鑄鐵(I)—製造實務”，QIT-Fer et Titane Inc., 碩建，1992。
25.潘國棟、廖高宇 譯，“球墨鑄鐵手冊”，中華民國鑄造學會，1994。
26.涂人福，“製程參數對低碳當量沃斯回火球墨鑄鐵機械性質的影
響”，國立臺灣師範大學工業教育學系碩士論文，2000。
27.毛世傑，“沃斯回火球墨鑄鐵技術手冊”，金屬工業發展研究中心，2000，pp.27-79。
28. Eugene C. Muratore, Chantall Labrecque and Martin Gagne, Development of Carbide Free Thin-Wall Ductile Iron Castings”, Proceedings of the 7th Asian Foundary Congress-Taipei, Taiwan, 2001, pp.153-167.
29.碩建股份公司 譯，“無碳化物薄壁球墨鑄鐵件之開發”，鑄造科技153期，2002，pp.4-10。
30. Dr. STEPHEN I.KARSAY 著，林良清、梁正華 編譯，“新編球墨
鑄鐵手冊(Ⅲ)”，中華民國鑄造學會，1988。
31.賴耿陽，“鑄造技術用書-鑄物設計”，復漢出版，1998，pp.158-159。
32.葉源達，“球狀石墨鑄鐵之製造”，財團法人臺北市徐氏基金會，1978。
33.“Feasibility of Exhaust Manifolds with ThinWalls on DISAMATIC”,DISA Internal Report on Trials from 3/2/94 to 3/15/94.
34. R. Dobbener, and K.J. Best, “Foundry Experiences in the Use of Late Mold-Inoculation for Production of Thin-Walled SG and CG Iron Castings,”SG Iron-The Next 40Years, 1987 BCIRA Conference, Apr 7-9, 1987.
35.潘永寧，“薄片縮狀石墨鑄鐵之研製”，鑄工45期，1987，pp.1-16。
36. G. Lesoult and J. Lacaze, “Inoculation of Spheroidal Graphite Cast Iron ”, Physical Metallurgy of Cast Iron V, Proceedings of the 5th International Symposium on Physical Metallugy of Cast Iron, Nacy, France,October, 1994, pp.277-284.
37.“開發設計階段的品質工程”，田口品質工程講座(1)，中國生產力中心，1990。
38.“品質評價的SN比”，田口品質工程講座(3)，中國生產力中心，
1991。
39.“田口式品質工程技術手冊(修訂版)”，中國生產力中心，1994。
40.“簡易田口品質工程”，中國生產力中心，1996。
41.“靜態參數設計”，經濟部工業局八十七年度工業技術人才培訓計畫講義，中國生產力中心，1996。
42.“動態參數設計”，經濟部工業局八十七年度工業技術人才培訓計畫講義，中國生產力中心，1996。
43.“允差設計”，經濟部工業局八十七年度工業技術人才培訓計畫講義，中國生產力中心，1996。
44.陳延昌，“紫外光原型件成型技術精敏化之研究”，國立臺灣師範大學工業教育學系碩士論文，2002。
45.邱弘興、姜禮德，“合金添加對球墨鑄鐵之顯微組織及機械性質的影響”，鑄工93期，1994，pp.1-21。
46.林啟瑞、潘永寧，“以實驗計畫法生產鑄態肥粒鐵球墨鑄鐵”，技術月刊，第五卷，第四期，1990，pp.371-381。
47.邱弘興 著，品質工程理論之分析及其應用研究，新科技書局，
1998。
48.洪敏雄 主編，工程材料試驗(Ⅰ)—金屬材料試驗，中國材料科學
學會，1999。
49.George F. Vander Voort, “METALLOGRAPHY— Principles and
Practice ”, 中央圖書，1984。
50.潘永寧 編譯，球墨鑄鐵金相圖集，中華民國鑄造學會，1986。