稻殼灰是在農業生產中的常見的廢棄物，本論文製備了P(AA/AM)/RHA複合水膠，並改變稻殼灰劑量和沒有添加稻殼灰的P(AA/AM)水膠比較，使用FT-IR來對水膠結構鑑定，SEM觀察表面型態，然後將水膠浸泡在去離子水、不同濃度的鹽水和孔隙溶液，測試水膠在不同環境的吸水率。
將P(AA/AM)/RHA複合水膠添加至水泥漿、水泥砂漿中，當作自養護劑，並比較一般的P(AA/AM)水膠和稻殼灰複合水膠，對於砂漿漿體中重量損失、內部濕度、乾縮變化、自體收縮、抗壓強度以及凝結時間的影響；以及水泥漿體的裂縫指數和水泥漿體的表面型態，探討水泥漿體的水化現象。
結果發現，P(AA/AM)/RHA複合水膠在鹽水溶液、孔隙溶液有較高的吸水率，而且對孔隙溶液有較好的保水率。將P(AA/AM)/RHA複合水膠加至水泥砂漿與水泥漿中，減少了水泥砂漿的重量損失、乾縮變化還有自收縮變化，改善了抗壓強度、內部濕度，對減少水泥漿的裂縫有不錯的效果。

Rice husk ash (RHA) was very common waste in agricultural production. In the thesis，we had prepared P(AA/AM)/RHA hydrogel composites, and changed the dosage of RHA, compared to P(AA/AM) hydrogel without RHA. FT-IR spectrum was used to identity the functional group of hydrogels. SEM was observed the surface of hydrogels. Then the hydrogels was determined water absorbency in deionized water、saline solution of different concentration and pore solution.
P(AA/AM)/RHA hydrogel composites were used as self-curing agent, added to cement paste and mortar. We compared mortar added to RHA composites with that added general P(AA/AM) hydrogel for the influences of weight-loss、relative humidity、drying shrinkage、autogenous shrinkage and setting time. Further, the cracking index in cement paste and the surface of cement paste were determined, observed and discussed cement hydration.
The results indicated that the higher water absorbency of all tested P(AA/AM)/RHA hydrogel composites in saline solution, and better water retention in pore solution. When P(AA/AM)/RHA composites was added to mortar and cement paste, it reduced weight-loss、drying shrinkage and autogenous shrinkage, improved compressive strength and internal humidity, lower cracking formation had good influences in cement paste.

1.Hasine, K., Saadet, Ö., Murat, O., Modified polyacrylamide hydrogels and their application in removal of heavy metal ions. Polymer, 44 (2003),1785–1793
2. Qingzhou C., Wei W., Baohua G, and Liyuan L., A Combined Physical−Chemical Polymerization Process for Fabrication of Nanoparticle−Hydrogel Sensing Materials., Macromolecules,45 (2012), 8382−8386
3. Elbadawy A. Kamoun , El-Refaie S. Kenawy , Xin Chen, A review on polymeric hydrogel membranes for wound dressing applications: PVA-based hydrogel dressings., J. Adv. Res.,8 (2017), 217–233 4. T. Thimma R., Atsushi, T., Simultaneous and sequential micro-porous semi-interpenetrating polymer network hydrogel films for drug delivery and wound dressing applications. Polymer ,50 (2009),3537–3546
5. Jenson,O.M. and P.F. Henson, Water-entrained cement-based materials II.Experimental observations. Cem. Concr. Res, 32 (2002),973-978
6. Xue-ping Chen, Guo-rong Shan, Jian Huang, Zhi-ming Huang, Zhi-xue Weng, Synthesis and Properties of Acrylic-Based Superabsorbent. Journal of Applied Polymer Science, 92 (2004), 619–624
7. P.J. Flory, Principle of polymer Chemistry,1953, Cornell University Press, United States.
8. O. Okay, General Properties of Hydrogels,2010, Springer, Germany.
9. Baker,J., H.Blanch, and J.Prausnitz,Swelling properties of acrylamide-based ampholytic hydrogels: Comprison of experiment with theory. Polymer-London, 36 (1995),1061
10. Qian Zhu, Effect Of Multivalent Ions On The Swelling And Mechanical Behavior Of Superabsorbent Polymers (Saps) For Mitigation Of Mortar Autogenous Shrinkage. Purdue University,2014
11. Ali Pourjavadi, Mehran K., Gholam R. M., Hossein H., Synthesis and super-swelling behavior of a novel protein based superabsorbent hydrogel, Polymer Bulletin 57 (2006), 813–824
12. Shimei Xu, Liqin Cao, Ronglan Wu, Jide Wang.,Salt and pH responsive property of a starch-based amphoteric superabsorbent hydrogel with quaternary ammonium and carboxyl group (II). J. Appl. Polym. Sci.,101 (2006), 1995-1999.
13. Chunyu C., Bo D., Jie C., Lina Z.,Superabsorbent hydrogels based on cellulose for smart swelling and controllable delivery. Eur. Polym. J.,46 (2009),92-100
14. A. Pourjavadi and H. Salimi, New Protein-Based Hydrogel with Superabsorbing Properties: Effect of Monomer, Ratio on Swelling Behavior and Kinetics
Ind. Eng. Chem. Res., 47 (2008), 9206–9213
15. Bing Q.,Jun-rong L., Hui-ning X., Bei-hai H., Li-ying Q., Preparation of Sodium Carboxymethylcellulose/Poly(methyl acrylate) IPN Hydrogels and Their Application for Adsorption., J. Appl. Polym. Sci.,131 (2014), 41101-41106
16. Ying Z., Haijia S., Li F., Tianwei T., Superabsorbent hydrogels from poly(aspartic acid) with salt-,temperature- and pH-responsiveness properties., Polymer ,46 (2005),5368–5376
17. Daniela P., Milena D. C. and Rolando B., Polysaccharide-Based Hydrogels: The Key Role of Water in Affecting Mechanical Properties., Polymers 2012, 4, 1517-1534
18. Hany El-Hamshary, Synthesis and water sorption studies of pH sensitive poly(acrylamide-co-itaconic acid) hydrogels, Eur. Polym. J., 43 (2007), 4830–4838
19. Alan Y. Kwok, Greg G. Qiao, David H. Solomon, Synthetic hydrogels. 1. Effects of solvent on poly(acrylamide) networks., Polymer ,44 (2003),6195–6203
20.Li,A., J.Zhang,and A. Wang, Synthesis,characterization and water absorbency properties of poly(acrylic acid)/sodium humate superabsorbent composite. Polym. Adv. Tech.,16 (2005),675-680.
21. Erdener Karadağ, Tayfun Kırıştı, Semiha Kundakcı, Ömer Barıs,Üzüm, Investigation of Sorption/Swelling Characteristics of Chemically Crosslinked AAm/SMA Hydrogels as Biopotential Sorbent, J. Appl. Polym. Sci.,117 (2010), 1787–1797
22. Y.M. Mohan, T. Premkumar, D.K. Joseph, K.E. Geckeler, Stimuli-responsive
poly(N-isopropylacrylamide-co-sodium acrylate) hydrogels: A swelling study in surfactant and polymer solutions., Reactive and Functional Polymers, 67 (2007), 844–858
23. Jia W., Shimei X., Ronglan W., Jide W., Yi G., Synthesis and Characteristics of an Amphoteric Semi-IPN Hydrogel Composed of Acrylic Acid and Poly(diallydimethylammonium chloride), J. Appl. Polym. Sci., 103 (2006), 345–350
24. Lee,W.F. and C.F. Chen. Poly(2-hydroxylethylmethacrylate-co-sulfobetaine) hydrogels. II.Synthesis and swelling behaviors of the [2-hydroxyethyl-methacrylate-co-3-dimethyl(methacryloyloxyethyl)ammonium propane sulfonate] hydrogels.J. Appl. Polym. Sci.,69 (1998),2021-2034
25. Shimei X., Ronglan W., Xiaojuan H., Liqin C., Jide W., Effect of the Anionic-Group/Cationic-Group Ratio on the Swelling Behavior and Controlled Release
of Agrochemicals of the Amphoteric, Superabsorbent Polymer Poly(acrylic acid-codiallyldimethylammonium chloride), J. Appl. Polym. Sci., 102 (2005), 986–991
26. Radhakumary Changerath,Prabha D. Nair,Suresh Mathew,C. P. Reghunadhan Nair, Poly(methyl methacrylate)-Grafted Chitosan Microspheres for
Controlled Release of Ampicillin., Journal of Biomedical Materials Research Part B: Applied Biomaterials,89 (2008),68-76
27. An Li, Aiqin Wang, Jianmin Chen, Studies on Poly(acrylic acid)/Attapulgite Superabsorbent Composites. II. Swelling Behaviors of Superabsorbent
Composites in Saline Solutions and Hydrophilic Solvent–Water Mixtures., J. Appl. Polym. Sci., 94 (2004), 1869–1876
28. Y. Zheng, P. Li, J. Zhang, A. Wang, Study on superabsorbent composite XVI.
Synthesis, characterization and swelling behaviors of
poly(sodium acrylate)/vermiculite superabsorbent composites, Eur. Polym. J., 43 (2007), 1691–1698
29. Maryam Irani, Hanafi Ismail, Zulkifli Ahmad. Hydrogel Composites Based on Linear Low-Density Polyethylene-g-Poly(acrylic acid)/Kaolin or Halloysite Nanotubes., J. Appl. Polym. Sci., 131 (2014),40101-40112
30. J. Lin, J. Wu, Z. Yang, M. Pu, Synthesis and Properties of Poly(acrylic acid)/Mica
Superabsorbent Nanocomposite, Macromol. Rapid Commun. ,22 (2001), 422–424
31. L. Zheng, S. Xu, Y. Peng, J. Wang and G. Peng, Preparation and swelling behavior of amphoteric superabsorbent composite with semi-IPN composed of poly(acrylic acid)/Ca-betonite/poly(dimethyldiallylammonium chloride).Polym. Adv. Tech.,18 (2007),194-199
32. Hamed Gharekhani., Ali O., Abdolreza M., Ahmad B., Superabsorbent hydrogel made of NaAlg-g-poly(AA-co-AAm) and ricehusk ash: Synthesis, characterization, and swelling kinetic studies. Carbohydrate Polymers, 168 (2017) ,1–13
33. Yan, B. ,Jianzhong M., Na Li Synthesis and swelling behaviors of sodium carboxymethyl cellulose-g-poly (AA-co-AM-co-AMPS)/MMT superabsorbent hydrogel, Carbonhydrate,1 (2011),76-82
34. Xuefeng Su, Guo Zhang, Kun Xu, Jihua Wang, Chunlei Song, Pixin Wang,The Effect of MMT/Modified MMT on the Structure and Performance of the Superabsorbent Composite, Polymer Bulletin, 60 (2007), 69–78
35. Francisco H. A. Rodrigues,Antonio G. B. Pereira, Andŕe R. Fajardo,Edvani C. Muniz, Synthesis and Characterization of Chitosan-graft-Poly(acrylic acid)/
Nontronite Hydrogel Composites Based on a Design of Experiments, J. Appl. Polym. Sci. 2013, 3480-3489.
36. 謝素蘭,陳清山,華根, 稻穀灰作為卜作嵐材料之研究, 桃園創新學報 第三十二期
37. Jean de S. Cândido, Antonio G.B. Pereira , André R. F., Nágila M.P.S. Ricardo , Judith P.A. Feitosa,Edvani C. Muniz , Francisco H.A. Rodrigues. Poly(acrylamide-co-acrylate)/rice husk ash hydrogel composites. II. Temperature effect on rice husk ash obtention, Composites: Part B ,2013,246–253
38. Gemma Rodrıguez de Sensale, Strength development of concrete with rice-husk ash, Cem.Concr. Comp.,2006, 158–160
39. G.A. Habeeb, M.M. Fayyadh, Rice Husk Ash Concrete: the Effect of RHA Average Particle Size on Mechanical Properties and Drying Shrinkage, Aus. J. Basic Appl. Sci.,2009,1616-1622.
40. Nguyen V. T., Guang Y., Klaas van Breugel, O. Copuroglu., Hydration and microstructure of ultra high performance concrete incorporating rice husk ash, Cem. Concr. Res., 2011 ,1104–1111
41. M.H. Zhang, R. Lastra, and V.M. Malhotra, Rice-Husk ash paste and concrete: some aspects of hydration and the microstructure of the interfacial zone between the aggregate and paste, Cem. Concr. Res., 41 (1996), 963-977,.
42.楊思廉, 工業化學概論, 高立圖書，台，1992
43. C. Jolicoeur, M. Simard, Chemical Admixture-Cement Interactions: Phenomenology and Physico-chemical Concepts, Cem. Concr. Comp.,1998, 87-101
44. S. Hanehara and K.Yamada, Interaction between cement and chemical admixture from the point of cement hydration, absorption behavior of admixture and paste rheology, Cem. Concr. Res.29 (1999), 1159-1165.
45. Kovler K.,and S.Zhutovsky, Overview and future trends of shrinkage research. Material Structures,39 (2006),827-847
46.Holt E. Contribution of mixture design to chemical and autogeneous shrinkage of concrete at early ages. Cem.Concr.Res.,35 (2005),464-472
47. Dhir RK, Hewlett PC, Lota JS, Dyre TD. An investigation into the feasibility of formulating ‘self-curing’ concrete. Mater. Struct.,1994,27,606–615.
48.Henkensiefken, R. et al.,Volume change and cracking in internally cured mixtures made with saturated lightweight assregate under sealed and unsealed conditions. Cem. Concr. Res.,2009,427-437
49. J. Justs, M.Wyrzykowski, D. Bajare, P. Lura, Internal curing by superabsorbent polymers in ultra-high performance concrete, Cem. Concr. Res., 2015, 82–90
50. Baoguo Han,Liqing Zhang,Jinping Ou, Smart and Multifunctional
Concrete Toward Sustainable Infrastructures., Springer, Germany
51. Viktor Mechtcherine,Hans-Wolf Reinhardt, Application of Superabsorbent
Polymers (SAP) in Concrete Construction, Springer, Germany
52.Rha,C.,et al.,Preparation and characterization of absorbent polymer-cement composite. Cem. Concr. Res,1999,231-236
53.Jenson,O.M. and P. Lura,Techniques and materials for internal water curing of concrete. Materials and Structures,2006,817-825
54. D. Shen, T. Wang, Y. Chen , M. Wang, G. Jiang, Effect of internal curing with super absorbent polymers on the relative humidity of early-age concrete, Const. Build. Mater.,106 (2015), 246–253
55. A.Assmann,H.W. Reinhardt, Tensile creep and shrinkage of SAP modified concrete. Cem. Concr. Res,58 (2014),179-185
56. H. Beushausen, M. Gillmer, M. Alexander, The influence of superabsorbent polymers on strength and durability properties of blended cement mortars. Cem. Concr. Com., 52 (2014),73–80
57. V. Mechtcherine , E. Secrieru, C. Schröfl, Effect of superabsorbent polymers (SAPs) on rheological properties of fresh cement-based mortars — Development of yield stress and plastic viscosity over time. Cem. Concr. Res., 67 (2015),52–65
58. Self-Sealing Cracks with Superabsorbent Polymer. Imperial College London.2014.〈http://www3.imperial.ac.uk/concretedurability/researchprojects/selfsealingconcrete〉.
59. 周佑霖，聚(丙烯酸/丙烯醯胺)/矽灰複合水膠的合成與性質研究，國立台灣師範大學，2015.
60. Venkatesan S., Sundaram Thiraviam,K. Subramani,S. S., Pragathiswaran C., and Stanley A. B., In Situ Disassembling Behavior of Composite Hydrogels for the
Efficient Removal of Crystal Violet Dye from Aqueous Solution. ISRN Polymer Science, 2014, Article ID 632348.
61.葉華,趙建青,張宇,吸水樹酯水泥機材料自養護外加劑的研究，華南理工大學學報,2003,41-44
62. H. Taylor, Cement Chemistry 2ed edition,ICE,United State,1997.
63. Bjontegaard,O.,T. Hammer,and E.Sellevold. Cracking in high performance concrete before setting, 1998.